Chinese | English Create new materials, coalesce all things in symbiosis.

High-Speed Rail, Aviation, Marine Interiors, and All-Aluminum Household & Ceiling Decoration

Solution

Thermosetting Formaldehyde-Free Plant-Based Adhesive Series


DK88

Mix Ratio100:25
ApplicationCurtain coating
Viscosity (25℃)15000-22000mPa·s
Roller Peel Strength (24h)≥40Nmm/mm
Open Time12-17min
Curing Speed4min @70°C to initial cure (Aluminum Honeycomb)


Room-Temperature Curing Formaldehyde-Free Plant-Based Adhesive Series


K20

Mix Ratio100:25
ApplicationCurtain coating
Viscosity (25℃)15000-20000mPa·s
Roller Peel Strength (24h)≥35N/mm 
Pot Life12-16min
Open Time60-65min
Pressing Time6-8h

K20A 

Mix Ratio100:25
ApplicationCurtain coating
Viscosity (25℃)20000-29000mPa·s
Roller Peel Strength (24h)≥35N/mm
Pot Life12-16min
Open Time60-65min
Pressing Time6-8h

K20D 

Mix Ratio100:25
Application
Curtain coating
Viscosity (25℃)8000-14000mPa·s
Roller Peel Strength (24h)≥35N/mm
Pot Life12-16min
Open Time60-65min
Pressing Time
6-8h

K22 

Mix Ratio100:25
ApplicationCurtain coating
Viscosity (25℃)16000-22000mPa·s
Roller Peel Strength (24h)≥35N/mm 
Pot Life7-11min
Open Time50-55min
Pressing Time6-8h

K27 

Mix Ratio100:20
ApplicationCurtain coating
Viscosity (25℃)15000-23000mPa·s
Roller Peel Strength (24h)≥50N/mm 
Pot Life9-15min
Open Time45-50min
Pressing Time8-10h

K27X 

Mix Ratio100:25
ApplicationCurtain coating / Manual application
Viscosity (25℃)20000-30000mPa·s
Roller Peel Strength (24h)≥50N/mm 
Pot Life16-20min
Open Time70-75min
Pressing Time6-8h

K45C 

Mix Ratio100:20
ApplicationCurtain coating
Viscosity (25℃)15000-23000mPa·s
Roller Peel Strength (24h)≥25N/mm 
Pot Life9-11min
Open Time50-55min
Pressing Time6-8h

K45X 

Mixing Ratio100:20
ApplicationCurtain coating / Manual application
Viscosity (25°C)23000-33000mPa·s
Roller Peel Strength (24h)≥25N/mm
Pot Life13-18min
Open Time60-85min
Pressing Time6-8h